题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Mg-Fe-LDHs纳米颗粒的合成及其阴离子交换容量的研究显示文摘采用液相共沉淀法合成了镁铁型层状双氢氧化物(简称Mg-Fe-LDHs)纳米颗粒,考察了粒子形貌、化学组成、晶体结构、阴离子交换容量及原料配比的影响.结果表明,所合成样品为片状纳米颗粒,化学组成与原料配比基本一致.在所研究的原料配比范围内,产品中n(Mg)∶n(Fe)在2∶1~4∶1范围内,产品具有水滑石层状六方晶系结构.随n(Mg)∶n(Fe)从2∶1增大到4∶1,粒径增大(从37.9nm增大到61.2nm),六方晶格参数a降低(变化范围为0.317~0.310nm),而六方晶格参数c增大(变化范围为2.380~2.412nm),层间距增大(从0.793nm增大到0.804nm),阴离子交换容量增大(从0.52mmol/g增大到1.28mmol/g) | 苏延磊 侯万国 孙德军 刘尚营 张春光 | 1999 | 高等学校化学学报1999，20，7： | 27 |
| 2 | γ-Al_2O_3表面原位合成Ni-Al-CO_3 LDHs研究显示文摘Ni-Al-CO3 LDHs/γ-Al2O3 have been prepared using an in-situ synthesis technique. NH3·H2O was chosen as activation agent of Al on the γ-Al2O3 surface as well as precipitant. Ni-Al-CO3 LDHs/γ-Al2O3 was synthesized by controlling the reaction conditions such as temperature, concentration of Ni2+ and initial pH. The crystalline structure, chemical composition and porous structure were characterized by means of XRD, FT-IR, TG-DTA, 27Al MAS-NMR and N2 adsorption-desorption. The resulting sample of Ni-Al-CO3 LDHs/γ-Al2O3 possesses higher specific area and narrower pore distribution, in which Ni-Al-CO3 LDHs are located on the surface of γ-Al2O3 and share the same Al-O bonds with the γ-Al2O3 lattice. Finally a possible structural model was proposed to account for the porous characters of Ni-Al-CO3 LDHs/γ-Al2O3. | 毛纾冰 李殿卿 张法智 David G.Evans 段雪 | 2004 | 无机化学学报2004，20，5： | 15 |
| 3 | 柠檬酸三钠对Co^(2+)-Ni^(2+)-Fe^(3+)-CO_3^(2-) LDHs形貌及其离子交换性能的影响显示文摘Co2+/Ni2+/Fe3+摩尔比为0.5/3/1,采用络合剂柠檬酸三钠协助均相沉淀技术,制备了Co2+-Ni2+-Fe3+-LDHs层状材料,研究了柠檬酸三钠用量对Co2+-Ni2+-Fe3+LDHs层间距及形貌的影响。在此基础上,研究了不同层间距和不同形貌Co2+-Ni2+-Fe3+-23CO--LDHs层状材料的离子交换性能,即Co2+-Ni2+-Fe3+-23CO-LDHs层状材料在Na Cl-HCl的离子交换体系中进行阴离子交换反应,生成Co2+-Ni2+-Fe3+-Cl–-LDHs层状材料。研究结果表明:当柠檬酸三钠用量为0.6~1.0 mmol/L时,所制备的LDHs层间距为0.776 nm,片层结构分散性较好,产物的较大层间距和较好形貌使其仍保持良好的离子交换性能,并通过离子交换反应可分别得到4Cl O-、24SO-、3NO-、4Mn O-及CH3(CH2)113SO-插层Co2+-Ni2+-Fe3+-LDHs层状衍生材料;当柠檬酸三钠用量在1.5 mmol/L时,所制备的LDHs层间距为0.770 nm和0.691 nm,片层结构团聚并成玫瑰花形貌,使得客体离子较难插入到层间,产物的离子交换性能降低;当柠檬酸三钠的量增加到3.0 mmol/L时,得到的LDHs层间距为0.681 nm,片层结构变小,团聚现象加剧,LDHs片完全交错生长成球状形貌,产物完全失去了离子交换性能。 | 马向荣 刘宗怀 | 2014 | 无机材料学报2014，29，12： | 13 |
| 4 | 纳米双羟基复合金属氧化物(LDHs)对聚氯乙烯(PVC)阻燃抑烟研究显示文摘总结了聚氯乙烯(PVC)塑料燃烧时产生烟雾的机理及其阻燃抑烟原理,并且在已开发出的常用无机阻燃抑烟剂的基础上研究了一种新型的无毒环保型无机纳米级阻燃抑烟剂———纳米双羟基复合金属氧化物(LDHs)。分析了其对PVC的阻燃抑烟机理,并且试验证实了它的阻燃抑烟效果。试验结果表明,该阻燃剂只需少量添加就有明显的阻燃抑烟效果,并且克服了以往由于大量添加无机阻燃剂而造成的力学性能下降的缺点,是一种很有发展前景的新型阻燃抑烟剂。 | 郑秀婷 吴大鸣 刘颖 朱复华 | 2004 | 塑料2004，33，3： | 13 |
| 5 | 层状双金属氢氧化物Zn(Cu)/Al-LDHs的制备及其光催化还原二氧化碳的研究显示文摘用共沉淀法制备了不同M2+/M3+的层状双金属氢氧化物Zn(Cu)/Al-LDHs,利用粉末X射线衍射(XRD)、扫描电子显微镜(SEM)、紫外可见漫反射(UV-Vis DRS)以及热重分析仪(TG-DSC)等测试方法表征了所制备样品的结构、形貌以及相关物性.在自行设计的催化反应系统中于室温和常压下测试了催化剂光催化还原CO2(g)+H2O(g)的活性.结果表明所制备的Zn(Cu)/Al-LDHs样品均可光催化还原CO2(g)+H2O(g),实验中测得的催化反应产物主要是CO和CH4.LDHs结构中Cu2+对Zn2+的取代导致催化剂吸收边红移,并显著提高催化反应产率. | 贺学智 李炳杰 吴志坚 陈威 袁坚 上官文峰 | 2013 | 分子催化2013，27，1： | 13 |
| 6 | Mg-Al LDHs改性沥青的制备与抗老化性能研究显示文摘将镁铝基层状双氢氧化物(Mg-Al LDHs)与基质沥青熔融共混,制备了Mg-Al LDHs改性沥青。采用薄膜烘箱试验(TFOT)和紫外光老化试验分别研究了不同掺量的Mg-Al LDHs对沥青短期热氧老化和紫外光老化性能的影响。结果表明,Mg-Al LDHs可有效抑制沥青在TFOT和紫外光老化过程中软化点和粘度的增加,显著提高沥青延度保留率,减小其质量变化,有效改善了沥青抗短期热氧老化和紫外光老化性能。 | 吴伟飞 李玉环 徐松 时敬涛 田翠芳 余剑英 | 2014 | 武汉理工大学学报2014，36，4： | 10 |
| 7 | LDHs/紫外吸收剂复合改性对沥青性能的影响研究显示文摘分别研究了层状双羟基复合金属氢氧化物(LDHs)及其与两种紫外吸收剂(UV-531和UV-284)复合改性对沥青物理性能、流变性能和抗紫外老化性能的影响。结果表明:与LDHs改性相比,LDHs与紫外吸收剂复合改性可有效抑制沥青的软化点、粘度和复数模量的增大,以及针入度、延度和相位角的减小;紫外老化后,相比于单掺LDHs或紫外吸收剂,LDHs/紫外吸收剂复合改性剂可进一步减小沥青的粘度老化指数、软化点增量和复数模量老化指数,表现出明显的协同效应,这可归因于LDHs和紫外吸收剂复合使用时,被LDHs反射的紫外光会被紫外吸收剂所吸收,从而避免了对沥青分子结构的破坏。 | 高丽 徐松 李玉环 马庆丰 薛理辉 余剑英 | 2015 | 武汉理工大学学报2015，37，1： | 10 |
| 8 | 硼酸根插层的Ca-Al-LDHs的制备、表征和应用显示文摘以四水硝酸钙、六水硝酸铝、氢氧化钠及硼酸为原料,利用离子交换的方法合成硼酸根插层的Ca-AlLDHs,并对其进行初步表征。X射线衍射、电子扫描电镜分析和红外光谱测试表明合成出的硼酸根插层Ca-AlLDHs具有良好的层状结构,形貌呈片状,插入钙铝层板间的硼酸根具有BO_4^(5-)和BO_3^(3-)两种结构。以硬脂酸、钛酸酯偶联剂NDZ-311为改性剂,对合成出的硼酸根插层的Ca-Al-LDHs进行改性,并将改性后的硼酸根插层的LDHs粉体与乙烯-醋酸乙烯酯(EVA)材料进行混合得到复合塑料,通过测复合塑料的氧指数研究该种LDHs的阻燃效果。发现当改性硼酸根插层的LDHs粉体填充量为40%(质量分数)时,拉伸强度为9.68 MPa,断裂伸长率为663.3%,极限氧指数为27.2%。 | 王娜 仲剑初 王洪志 | 2016 | 无机盐工业2016，48，1： | 9 |
| 9 | 功能化层状双金属氢氧化物材料的应用进展显示文摘层状双金属氢氧化物(LDHs)因其优异的性能特别是低成本和结构与组成的可调控性在诸多领域备受关注。LDHs表面的正电荷性质、多羟基以及层间可以进行插层反应等使其较容易与不同的有机分子或有机无机纳米材料进行复合形成功能化层状纳米材料,这更进一步扩展了其应用范围。本文综述了近几年功能化LDHs在传感、催化、超级电容、废水处理及光致发光等方面的应用进展,并总结分析了在这些领域中应用的特点和作用。 | 任锦 梁良 周瑜 张磊 余敬谋 | 2019 | 材料科学与工程学报2019，37，3： | 9 |
| 10 | Ni/Zn/Cr系复合金属氧化物的制备及其光催化还原二氧化碳性能研究显示文摘以共沉淀法合成的Ni/Zn/Cr系层状金属氢氧化物(LDHs)经不同温度焙烧获得相应的复合金属氧化物,利用XRD、TG、XPS、TEM、BET和UV-Vis等表征手段对所制备样品的结构、组成、形貌以及吸光特性等进行了分析,并考察了样品在常温常压下光催化还原CO2(g)+H2O(g)的性能.结果表明,以Ni/Zn/Cr-LDHs为前驱体经5 00℃焙烧后可得到晶粒尺寸小、分散均匀度高的多相复合金属氧化物,主晶相为纳米尺度的NiO、Cr2O3、ZnCr2O4和NiCr2O4,在这些金属氧化物的协同作用下,样品表现出较好的光催化还原二氧化碳活性,主产物为CH4和CO. | 李炳杰 吴志坚 陈澍 上官文峰 袁坚 | 2014 | 分子催化2014，28，3： | 8 |
| 11 | 载体树脂、分散剂及剪切速率对纳米粉体在高聚物中的分散效果的影响显示文摘选择不同的载体树脂和分散剂 ,研究了阴离子型层状纳米材料 (LDHs)在载体树脂中的分散及剪切对分散效果的影响 ,结果表明 ,LDHs在EVA中分散均匀 ;分散剂B的加入使LDHs在EVA中的分散更均匀 ;剪切能使团聚状LDHs基本消失 ,LDHs的粒径可达到十几纳米。 | 王红杰 吴大鸣 刘颖 张蕾 段雪 | 2001 | 塑料工业2001，29，6： | 8 |
| 12 | Performance of halogen-free flame retardant EVA/MH/LDH composites with nano-LDHs and MH显示文摘The flammability properties of three series of Ethylene-Vinyl Acetate/Magnesium Hydroxide/Layered Double Hydroxide(EVA/MH/LDH) composites as well as the flame retardance effect between LDH and the conventional flame retardant additive MH are investigated.In addition to acting as an insulating barrier,LDH assists the dispersion of MH particles in the EVA matrix,and promotes the formation of the char residues because of its abundant interlayer hydroxyl groups.Composites containing LDH show good flame retardancy in Cone and LOI testings.This means that the combustion properties of the composites have decreased,which may lessen the fire hazard when this materials are used. | DING YanYan XU Liang HU GengSheng | 2011 | Chinese Science Bulletin2011，56，35： | 8 |
| 13 | 以钢渣为原料合成层状双氢氧化物及其结构表征显示文摘以钢渣为原料,醋酸为浸出介质,在一定条件下得到浸出液,利用共沉淀法合成了Ca-Mg-Al-Fe四元层状双金属氢氧化物(LDHs),探讨了pH、晶化温度和晶化时间对Ca-Mg-Al-Fe四元LDHs层状材料合成的影响,采用XRD、XRF、SEM、FT-IR、TEM、DTA/TG和BET对样品进行了表征。研究表明,pH对层状材料合成的影响最大,pH在10.5~11.8可形成纯相水滑石;晶化温度和晶化时间是影响晶格参数和层间距的重要因素,随温度及时间的增加,其晶格参数a、c及层间距均先减小后增大;LDHs的晶粒尺寸沿a轴方向比沿c轴方向大。当pH=11.8,晶化温度150℃,晶化时间16 h时,合成的LDHs层状材料结构规整、晶型良好、层状结构明显、孔径较大且热稳定性良好。 | 陈艳 王丽秋 王晨晔 李会泉 | 2015 | 化工学报2015，66，12： | 6 |
| 14 | Effect of Layered Double Hydroxides on Ultraviolet Aging Resistance of SBS Modified Bitumen Membrane显示文摘Layered double hydroxides(LDHs)/styrene-butadiene-styrene(SBS) copolymer modified bitumen was prepared by melt blending. The effect of LDHs on the ultraviolet(UV) aging behavior of SBS modifi ed bitumen was investigated. The changes of chemical structures of modifi ed bitumen before and after UV aging were characterized by Fourier transform infrared spectroscopy(FTIR). The results show that LDHs obviously reduce the variation of softening point and low temperature fl exibility of SBS modifi ed bitumen under different UV radiation intensities, which indicates that the UV aging resistance performance of SBS modifi ed bitumen is improved effectively by LDHs. Compared with SBS modifi ed bitumen, the changes of carbonyl, sulfoxide and butadienyl of LDHs/SBS modified bitumen decrease significantly after UV aging according to FTIR analysis, demonstrating that the oxidation and degradation reactions of SBS modifi ed bitumen were restrained effectively by adding LDHs. | 徐松 余剑英 XUE Lihui SUN Yubin XIE Dong | 2015 | Journal of Wuhan University of Technology(Materials Science)2015，30，3： | 6 |
| 15 | 镁合金表面缓蚀剂插层LDHs涂层自愈合性能的研究显示文摘通过水热法在AZ31镁合金表面原位合成层状双氢氧化物(LDHs)膜MgAl-LDHs-NO3,采用阴离子交换反应将钨酸根阴离子(WO42-)和半胱氨酸(Cys)阴离子嵌入LDHs层间,制得MgAl-LDHs-WO4和MgAl-LDHs-Cys。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、能谱仪(EDS)、电化学阻抗测试(EIS)研究了膜层的形貌、结构、耐蚀性和自愈合性能。结果表明,在3.5%(质量分数)NaCl溶液中3种膜层的耐蚀性由强到弱依次为LDHs-WO4>LDHs-Cys>LDHs-NO3。预制划痕后在3.5%NaCl溶液中浸泡,实验结果表明,3种膜层均表现出良好的自愈合能力,电化学结果显示浸泡8 d时耐蚀性最佳,随后呈下降趋势,且LDHs-WO4和LDHs-Cys自愈合能力明显优于LDHs-NO3。这是由于LDHs-WO4和LDHs-Cys含有缓蚀性阴离子,膜层不仅阻隔溶液对基体的腐蚀,而且LDHs的层间结构还可以释放缓蚀性离子,这些离子与镁结合形成难溶沉淀,促进膜层的自愈合过程。 | 孙俊丽 李思远 许恒旭 侯利锋 杜华云 刘宝胜 卫英慧 | 2020 | 稀有金属材料与工程2020，49，12： | 6 |
| 16 | Recent progress in polymer/layered double hydroxide nanocomposites显示文摘在 nanocomposites 的研究的新开发基于最近的年里的聚合物矩阵和分层的双氢氧化物(LDH ) 被考察联合我们的相对研究工作,合成技术,物理化学的描述,和改进材料性质特别在之中被讨论。polymer/LDH nanocomposites 的可能的申请也被建议。 | DING Peng CHEN Wei QU Baojun | 2006 | Progress in Natural Science:Materials International2006，16，6： | 5 |
| 17 | 一种新型复配体系对ABS树脂的阻燃性能研究显示文摘丙烯腈(Acrylonitrile)-丁二烯(Butadiene)-苯乙烯(styrene)共聚物,即ABS树脂,是一种重要的工程塑料,然而其极易燃烧的性质在很大程度上限制了其的广泛应用。本文采用膨胀型阻燃剂—[4-(二苯氧基-磷酰基氨基)-6-苯基-[1,3,5]三嗪-2-基]氨基磷甲酸二苯基酯(DPCPB)和纳米级三元水滑石粉粒Mg-Al-Co-LDHs组成复配体系,对ABS树脂进行阻燃研究。实验结果表明,新型膨胀型阻燃剂DPCPB能够有效阻燃ABs树脂,在配方ABS/DPCPB=100/25,ABS/DPCPB/LDHs=100/21/4的添加条件下.复合材料的极限氧指数(LOI)从纯ABS树脂的18.1分别提高到23.9、24.7,同时垂直燃烧实验UL-94分别通过V-2、V-1级测试。而不同材料的热失重曲线(TGA)表明,新型阻燃体系同时具备气相与凝聚相双重阻燃机理,可显著提高复合材料燃烧后的残炭产量,Mg-Al-Co-LDHs的添加能够与DPCPB产生良好的协效阻燃作用。 | 刘伟 陈永斌 周涛 李思敏 姚玉婷 | 2015 | 新型工业化2015，5，2： | 5 |
| 18 | 硼酸根插层锌镁铝水滑石的制备及其阻燃抑烟性能研究显示文摘采用成核/晶化隔离法和离子交换法分别制备了处于纳米尺寸的碳酸根镁铝水滑石和硼酸根锌镁铝水滑石。并将两种水滑石加入到聚醋酸乙烯脂中制备成复合材料,测试了复合材料的氧指数和无焰燃烧条件下的烟密度,考察了纳米LDHs对聚醋酸乙烯脂的阻燃及抑烟效果,并探讨了阻燃和抑烟机理。 | 李素锋 李殿卿 史翎 Evans D.G. 段雪 | 2005 | 阻燃材料与技术2005，，4： | 5 |
| 19 | One-Pot Microwave-Assisted Synthesis of Graphene/Layered Double Hydroxide(LDH) Nanohybrids显示文摘A facile and rapid method to synthesize graphene/layered double hydroxide(LDH)nanohybrids by a microwave technique is demonstrated.The synthesis procedure involves hydrothermal crystallization of Zn–Al LDH at the same time in situ reduction of graphene oxide(GO)to graphene.The microstructure,composition,and morphology of the resulting graphene/LDH nanohybrids were characterized.The results confirmed the formation of nanohybrids and the reduction of graphene oxide.The growth mechanism of LDH and in situ reduction of GO were discussed.The LDH sheet growth was found to prevent the scrolling of graphene layers in resulting hybrids.The electrochemical properties exhibit superior performance for graphene/Zn–Al LDH hybrids over pristine graphene.The present approach may open a strategy in hybridizing graphene with multimetallic nano-oxides and hydroxides using microwave method. | Sunil P.Lonkar Jean-Marie Raquez Philippe Dubois | 2015 | Nano-Micro Letters2015，7，4： | 5 |
| 20 | 微波法合成层-层分离的镍铝水滑石/石墨烯超薄大片复合材料及其超级电容器电极性能(英文)显示文摘本文通过微波加热法设计合成了水滑石-石墨烯复合材料,并对该材料进行了表征.研究发现,通过微波法合成的水滑石-石墨烯复合材料具有超薄大片结构,是一种'层-层'剥离的结构,该结构有利于减少石墨烯的团聚,形成大规模片状水滑石材料.对材料的电容性能表征发现,该材料具有优异的充放电性能及良好的电化学稳定性,是一种有潜力的超级电容器电极材料. | 王卓 贾巍 蒋梦蕾 陈晨 李亚栋 | 2015 | Science China Materials2015，58，12： | 5 |