题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Preparation and Performance of Salt Tolerance and Thermal Stability Cellulose Nanofibril Hydrogels and Their Application in Drilling Engineering显示文摘The poor salt tolerance,thermal stability,and environmental performance of petrochemicals can severely limit their applications in drilling engineering.In this study,cellulose nanofibril(CNF)hydrogels with improved salt tolerance and thermal stability were prepared,and their filtration performance was evaluated.The hydrogels were prepared through the simultaneous grafting of 2-acrylamido-2-methylpropane sulfonic acid(AMPS)and butyl acrylate(BA)onto the CNF surface through ceric ammoniumnitrate-induced radical polymerization.The modified and original CNF samples were characterized using Fourier Transform infrared spectroscopy(FT-IR)and rheological measurements.The FT-IR analysis results showed that both AMPS and BA were grafted onto the CNF backbone,affirming the successful preparation of the grafted CNFs.The rheological analysis results showed that the modified CNF hydrogels exhibited significantly improved salt tolerance,thermal stability,and“salt-thickening”effect.Moreover,the results of the fluid loss test showed that the modified CNF hydrogels exhibited a much better fluid loss control than the original CNF hydrogels.In addition,after adding 2%modified CNF hydrogels as a filtrate reducer in the drilling fluids prepared with a 6%combined salt solution,the filtrate loss was significantly reduced even after aging for 72 h at 160℃. | XiongLi Liu An Wang ChunPing Wang JiaLei Qu YangBing Wen Bin Chen ZhongGuang Wang BinBin Wu ZhaoYang Yuan Bing Wei | 2019 | Paper And Biomaterials2019，4，2： | 7 |
| 2 | Application of Cellulose and Cellulose Nanofibers in Oil Exploration显示文摘In this article, the application of cellulose and cellulose nanofibers in oil exploration was discussed, and the research status of using cellulose and cellulose nanofibers as oil displacement agents, oil-well cementing additives, and foam stabilizers were summarized. | Xiongli Liu Chunping Wang An Wang Jialei Qu Yangbing Wen Bing Wei | 2019 | Paper And Biomaterials2019，4，3： | 2 |
| 3 | Stabilizing Pickering Emulsions Using Octenyl Succinic Anhydride Modified with Cellulose Nanofibrils显示文摘In this study,(2,2,6,6-tetramethylpiperidin-1-yl)oxyl-mediated(TEMPO-mediated)oxidized cellulose nanofibrils(TOCNFs)modified with octenyl succinic anhydride(OSA)to improve their hydrophobicity and emulsification performance were investigated.OSA loadings of 9.87-14.81 mmol/g(base on oven-dry weight of TOCNFs)were explored during modification,and the obtained OSA-modified TOCNFs(TOCNF-OSA)were characterized using Fourier transform infrared spectroscopy,X-ray photoelectron spectroscopy,X-ray diffraction,and thermogravimetric analysis.Additionally,the emulsification performance of TOCNF-OSA was also investigated in the preparation of the Pickering emulsion.The results demonstrated that the molecular chain of OSA was successfully grafted onto the backbone of TOCNFs during modification.With an increase in OSA loading,the content of the carboxyl group of the modified TOCNF-OSA increased significantly while the Zeta potential decreased.Moreover,a degree of substitution of 0.95 could be achieved at an OSA loading of 14.81 mmol/g.During the preparation of Pickering emulsions,compared with original TOCNFs,the modified TOCNF-OSA significantly improved the stability and dispersibility of the Pickering emulsion.This study demonstrated a promising approach for the modification of the Pickering emulsion to produce an eco-friendly emulsifier with superior performance for use in the food industry. | Jialei Qu Langman Luo Weifeng Zhang Shao Geng Chunping Wang An Wang Yangbing Wen | 2022 | Paper And Biomaterials2022，7，3： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员