| 1 | Mechanical, tribological and anti-corrosive properties of polyaniline/graphene coated Mg-9Li-7Al-1Sn and Mg-9Li-5Al-3Sn-1Zn alloys显示文摘The mechanical,tribological and corrosion protection offered to Mg-9Li-7Al-1Sn and Mg-9Li-5Al-3Sn-1Zn alloys by the epoxy coating containing polyaniline/graphene(PANI/Gr)pigments is undertaken in the current work.PANI/Gr containing coatings were observed to be strongly adherent with a higher scratch hardness(Hs)and plowing hardness(Hp),i.e.Hsof 0.43 GPa,and Hpof 0.61 GPa,respectively when compared to that of neat epoxy coating(Hsof 0.17 GPa,and Hpof 0.40 GPa,respectively).Due to their higher Hsand Hpvalues,PANI/Gr based coatings displayed an enhanced wear resistance(Wear volume,Wv=4.53×10^-3 m^3)than that of neat epoxy coating(Wv=5.15×10^-3 m^3).The corrosion protection efficiency in corrosive environment of 3.5 wt%NaCl solution was obtained to be>99% for PANI/Gr containing coatings when compared to that of neat epoxy coating.The charge-transfer resistance(R(ct))of the PANI/Gr containing coatings were estimated to be>10^6 cm^2,which indicates their highly protective nature when compared to that of neat epoxy coating(R(ct)10^5 Ω cm^2).Hence,PANI/Gr containing coatings can be potentially used for wear resistance and corrosion protection applications in marine environments. | Rita Maurya Abdul Rahim Siddiqui Prvan Kumar Katiyar Kantesh Balani | 2019 | Journal of Materials Science & Technology2019，35，8： | 4 |
您所在的机构暂未开通此部分的功能，请联系管理员