| 2 | Eutectic-reaction brazing of Al_(0.3)CoCrFeNi high-entropy alloys using Ni/Nb/Ni interlayers显示文摘In this study,a novel eutectic-reaction brazing of Al_(0.3)CoCrFeNi high-entropy alloys(HEAs)^(1)was investigated with a design of laminated Ni/Nb/Ni interlayers.The typical Al_(0.3)CoCrFeNi brazing seam consisted of proeutecticγ,the lamellar eutectic structure composed of face-centered cubic(FCC)phase(eutecticγ)and C14 Laves,as well as a few amounts of Nb based solid solution.A high density of nanoscale ordered L1_(2)(γ)phase was precipitated withinγphase matrix.With the brazing temperature raised from 1200 to 1320℃,the dissolution volume of Al_(0.3)CoCrFeNi alloy into Ni-Nb liquid was increased.The microstructure of the brazing seam changed from hypereutectic(blocky Laves+γphase)to eutectic(Laves+eutecticγ)to hypoeutectic structures(proeutecticγ+Laves/γeutectic structure).The shear strength of joints was increased gradually due to the formation of eutectic lamellae and the cellular growth of proeutecticγphase.The maximum shear strength of the joint brazed at 1320℃for 10 min was up to 592 MPa,reaching 95%of the base metal.The joint mainly ruptured in the soft proeutecticγphase in a ductile fracture mode. | Y.Lei J.Sun X.G.Song M.X.Yang T.L.Yang J.Yin | 2022 | Journal of Materials Science & Technology2022，，26： | 1 |
| 4 | A Superconducting Magnet with Center Field of 10 T and φ100 mm Warm Bore显示文摘Aconduction-cooled superconducting magnet with central field of 10Tand warmbore of 100 mmwas designed based on a Nb3Sn and two NbTi superconducting coils.At the first stage,the NbTi coils havebeen fabricated andtested.Atwo-stage 4 KGifford-McMahon(GM) cryocooler withthe second-stage powerin1W,4.2Kis used to cool the magnet fromroomtemperature to 4 K.The superconducting magnet with thesame power supply has the operating current of 116A.The magnet can be rotated with a support frame to beoperated with either horizontal or vertical position.Apair of Bi-2223 hightemperature superconductingcurrentleads was employedto reduce heat leakage into 4.2Klevel.The NbTi coils reachto the operating current of120Awithout training effect to be observed duringchargingof the magnet during40 minutes chargingtime andgenerate the center field of 6.5T.The training effect inthe NbTi magnet directly cool-down by cryocooler andinter-winding support structure in magnet can be remarkablyimproved.The superconducting magnet has beenstably operatedfor more than 275 hours with 6.5T.In this paper,the detailed design,fabrication,stressanalysis and quench protection characteristics are presented. | Q.Wang L.Yan B.Zhao S.Song Y.Dai Y.Lei H.Wang H.-C.Huang | 2006 | 电工电能新技术2006，25，4： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员