| 4 | Synthesis of a Novel TiO_(2)@Ag_(3)PO_(4)Core-Shell Structure with Enhanced Photocatalytic Performance显示文摘Ag_(3)PO_(4)exhibits a high photocatalytic activity if exposed to visible light,however,it displays bottlenecks such as poor cycle-stability and mediocre ability to degrade methyl orange(MO)because of limited adsorption of MO molecules onto its surface.In this study,nano TiO_(2)prepared by a one-step method was combined with Ag_(3)PO_(4)to form a TiO_(2)@Ag_(3)PO_(4)heterojunction in order to improve this material both in terms of photocatalysis and photostability.After adding a KH-570 silane coupling agent,the photocatalytic performance of TiO_(2)@Ag_(3)PO_(4)could be improved even further,with the degradation rate of MO maintained at more than 90%after three cycles of visible in light. | Chao Wei Zhongjin Peng Yunfei Chen Yanhai Cheng | 2022 | Fluid Dynamics & Materials Processing2022，18，4： | 0 |
| 5 | A Nitride-Reinforced NbMoTaWHfN Refractory High-Entropy Alloy with Potential Ultra-High-Temperature Engineering Applications显示文摘Refractory high-entropy alloys(RHEAs)have promising applications as the new generation of hightemperature alloys in hypersonic vehicles,aero-engines,gas turbines,and nuclear power plants.This study focuses on the microstructures and mechanical properties of the NbMoTaW(HfN)_(x)(x=0,0.3,0.7,and 1.0)RHEAs.The alloys consist of multiple phases of body-centered cubic(BCC),hafnium nitride(HfN),or multicomponent nitride(MN)phases.As the x contents increase,the grain size becomes smaller,and the strength gradually increases.The compressive yield strengths of the NbMoTaWHfN RHEA at ambient temperature,1000,1400,and 1800℃ were found to be 1682,1192,792,and 288 MPa,respectively.The high-temperature strength of this alloy is an inspiring result that exceeds the high temperature and strength of most known alloys,including high-entropy alloys,refractory metals,and superalloys.The HfN phase has a significant effect on strengthening due to its high structural stability and sluggish grain coarsening,even at ultra-high temperatures.Its superior properties endow the NbMoTaWHfN RHEA with potential for a wide range of engineering applications at ultra-high temperatures.This work offers a strategy for the design of high-temperature alloys and proposes an ultra-high-temperature alloy with potential for future engineering applications. | Yixing Wan Yanhai Cheng Yongxiong Chen Zhibin Zhang Yanan Liu Haijun Gong Baolong Shen Xiubing Liang | 2023 | Engineering2023，，11： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员