Improvement of titanium alloy TA19 fatigue life by submerged abrasive waterjet peening:Correlation of its process parameters with surface integrity and fatigue performance

查看全文 作　　者：Gongyu [1]WANG;Shulei [1]YAO;Yuxin [1]CHI;Chengcheng [2]ZHANG;Ning [1]WANG;Yalong [2]CHEN;Rongsheng [1]LU;Zhuang [1]LI;Xiancheng [1]ZHANG

机构地区：[1]Key Laboratory of Pressure Systems and Safety,Ministry of Education,School of Mechanical and Power Engineering,East China University of Science and Technology,Shanghai 200237,China;[2]AECC Commercial Aircraft Engine Co.LTD,Shanghai Engineering Research Center for Commercial Aircraft Engine,Shanghai 201108,China

出　　处：《Chinese Journal of Aeronautics》索引2024年第37卷第1期,共14页

基　　金：supported financially by the National Natural Science Foundation of China(Nos.52275148 and U21B2077);Natural Science Foundation of Shanghai(20ZR1415300);Innovation Program of Shanghai Municipal Education Commission(2019-01-07-00-02-E00068);Innovation Program Phase II of AECC Commercial Aircraft Engine Co.Ltd.(Grant No.HT-3RJC1053-2020)。 摘　　要：Submerged abrasive waterjet peening(SAWJP)is an effective anti-fatigue manufacturing technology that is widely used to strengthen aeroengine components.This study investigated the correlation of SAWJP process parameters on surface integrity and fatigue life of titanium alloy TA19.SAWJP with different water pressures and standoff distances(SoDs)was conducted on the TA19 specimens.The surface integrity of the specimens before and after SAWJP with different process parameters was experimentally studied,including microstructure,surface roughness,microhardness,and compressive residual stress(CRS).Finally,fatigue tests of the specimens before and after SAWJP treatment with different process parameters were carried out at room temperature.The results highlighted that the fatigue life of the TA19 specimen can be increased by 5.46,5.98,and 6.28 times under relatively optimal process parameters,which is mainly due to the improved surface integrity of the specimen after SAWJP treatment.However,the fatigue life of specimens treated with improper process parameters is decreased by 0.55 to 0.69 times owing to the terrible surface roughness caused by the material erosion.This work verifies that SAWJP can effectively improve the surface integrity and fatigue life of workpieces,and reveals the relationship between process parameters,surface integrity,and fatigue life,which provides support for the promotion of SAWJP in the manufacturing fields. 关键词：Fatigue testing Process parameters Submerged abrasive waterjet peening Surface integrity Surface treatment Titanium alloy TA19

相关文献

参考文献（45）
引证文献（1）
耦合文献（7）

参考文献(45)

引证文献(1)

耦合文献(7)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Improvement of titanium alloy TA19 fatigue life by submerged abrasive waterjet peening:Correlation of its process parameters with surface integrity and fatigue performance

参考文献(45)

引证文献(1)

耦合文献(7)

用户提示