Low-temperature SCR activity and SO_2 deactivation mechanism of Ce-modified V_2O_5–WO_3/TiO_2 catalyst

查看全文 作　　者：Ziran [1,2]Ma;Xiaodong [1]Wu;Ya [1]Feng;Zhichun [3]Si;Duan [1,3]Weng;Lei [4]Shi

机构地区：[1]The Key Laboratory of Advanced Materials of Ministry of Education,School of Materials Science and Engineering,Tsinghua University;[2]National Institute of Clean-and-Low-Carbon Energy(NICE);[3]Advanced Materials Institute,Graduate School at Shenzhen,Tsinghua University;[4]Redbud Innovation Institute

出　　处：《Progress in Natural Science:Materials International》索引2015年第25卷第4期,共11页

基　　金：financial support from the National Science Foundation (No. 51202126);the Key Laboratory of Solid Waste Reuse for Building Materials (SWR-2013-003) 摘　　要：The promotion effect of ceria modi fi cation on the low-temperature activity of V2O5-WO3/TiO2 catalyst was evaluated for the selective catalytic reduction of NO with NH3(NH3-SCR). The catalytic activity of 1 wt% V2O5-WO3/TiO2 was signi fi cantly enhanced by the addition of 8 wt%ceria, which exhibited a NO x conversion above 80% in a broad temperature range 190–450 1C. This performance was comparable with 3 wt%V2O5-WO3/TiO2, indicating that the addition of ceria contributed to reducing the usage of toxic vanadia in developing low-temperature SCR catalysts. Moreover, V1 Ce WTi exhibited approximately 10% decrease in NOx conversion in the presence of 60 ppm SO2. The characterization results indicated that active components of V, W and Ce were well dispersed on TiO2 support. The synergetic interaction between Ce and V species by forming V–O–Ce bridges enhanced the reducibility of VCe WTi catalyst and thus improved the low-temperature activity. The sulfur poisoning mechanism was also presented on a basis of the designed TPDC(temperature-programmed decomposition) and TPSR(temperatureprogrammed surface reaction) experiments. The deposition of(NH4)2SO4on V1 Ce WTi catalyst was much smaller compared with that on V1 Ti.On the other hand, the oxidation of SO2 to SO3was signi fi cantly promoted on the CeO2-modi fi ed catalyst, accompanied by the formation of cerium sulfates. Therefore, the deactivation of this catalyst was mainly attributed to the vanishing of the V–Ce interaction and the sulfation of active ceria. 关键词：V2O5-WO3/TIO2 CERIA NH3-SCR LOW-TEMPERATURE activi

相关文献

参考文献（43）
引证文献（36）
耦合文献（0）

参考文献(43)

引证文献(36)

互联网出版许可证新出网证(渝)字10号全国400电话 - 免长途话费

Low-temperature SCR activity and SO_2 deactivation mechanism of Ce-modified V_2O_5–WO_3/TiO_2 catalyst

参考文献(43)

引证文献(36)

用户提示