| 1 | Prelithiation strategies for silicon-based anode in high energy density lithium-ion battery显示文摘Green energy storage devices play vital roles in reducing fossil fuel emissions and achieving carbon neutrality by 2050.Growing markets for portable electronics and electric vehicles create tremendous demand for advanced lithium-ion batteries(LIBs)with high power and energy density,and novel electrode material with high capacity and energy density is one of the keys to next-generation LIBs.Silicon-based materials,with high specific capacity,abundant natural resources,high-level safety and environmental friendliness,are quite promising alternative anode materials.However,significant volume expansion and redundant side reactions with electrolytes lead to active lithium loss and decreased coulombic efficiency(CE)of silicon-based material,which hinders the commercial application of silicon-based anode.Prelithiation,preembedding extra lithium ions in the electrodes,is a promising approach to replenish the lithium loss during cycling.Recent progress on prelithiation strategies for silicon-based anode,including electrochemical method,chemical method,direct contact method,and active material method,and their practical potentials are reviewed and prospected here.The development of advanced Si-based material and prelithiation technologies is expected to provide promising approaches for the large-scale application of silicon-based materials. | Tianqi Jia Geng Zhong Yao Lv Nanrui Li Yanru Liu Xiaoliang Yu Jinshuo Zou Zhen Chen Lele Peng Feiyu Kang Yidan Cao | 2023 | Green Energy & Environment2023，8，5： | 0 |
| 2 | Single-atomic Zn-(C/N/O)lithiophilic sites induced stable lithium plating/stripping in anode-free lithium metal battery显示文摘For anode-free lithium metal battery,lithiophilic surface modification on the current collector can effectively reduce the lithium nucleation barrier,so as to regulate the electrodeposition of lithium.Here,atomically dispersed Zn-(C/N/O)lithiophilic sites in the amorphous carbon medium were introduced onto Cu by an in-situ induced ion coordination chemistry strategy to get the modified Zn@NC@RGO@Cu current collector.X-ray absorption spectroscopy(XAS)combined with scanning transmission electron microscopy in high angle annular dark field(STEM-HAADF)analysis proved the single atomic state of the zinc sites surrounded by C,N,and O with a coordination number of~3.According to the electrochemical tests and first principle calculations,the ultra-uniformly dispersed Zn-(C/N/O)sites at the atomic level can effectively improve the lithium affinity,reduce the energy barrier for lithium nucleation,homogenize the lithium nucleation,and enhance an inorganic lithium compounds rich solid electrolyte interphase layer.As a result,the nucleation overpotential of lithium on the modified current collector was reduced to 7.7 mV,which was 5.4 times lower than that on bare Cu.Uniform lithium nucleation and deposition enabled stable Li plating/stripping and elevated Coulombic efficiency of 98.95%in Li||Cu cell after>850 cycles.Capacity retention of 89.7%was successfully achieved in the anode-free lithium metal battery after 100 cycles. | Shifei Huang Sirong Lu Yao Lv Nanrui Li Zhenwei Wu Geng Zhong Xiaolong Ren Yufeng Wang Bo Sun Yuxiong Huang Feiyu Kang Yidan Cao | 2023 | Nano Research2023，16，8： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员