| 2 | Enhanced strength and ductility in Ti46Al4Nb1Mo alloys via boron addition显示文摘To improve the strength and ductility of Ti Al alloys by second phase, Ti46 Al4 Nb1 Mo alloys doped with different B content(0.4%, 0.8%, 1.2%, 1.6% and 2.0%, atomic percent, hereafter in at.%, referred to as TNMx B) were prepared. Macro/microstructure evolution, mechanical properties and deformation mechanisms of the alloys were studied systematically. Results showed that the microstructure of TNM-0.4 B and TNM-0.8 B alloy remained columnar dendrites, and the secondary dendritic arms of columnar grains were more obvious. When the content of B is 1.2%, the columnar dendrites transformed to equiaxed grains, and theα2/γ lamellae colony size was further refined in TNM-1.6 B and TNM-2.0 B alloy. The morphologies and kinds of the borides were changed with increasing B content, XRD results showed that Ti B phase appeared with 1.6%B content, and both Ti B and Ti B2 phase formed in TNM-2.0 B alloy. There were straight and curved Ti B phases located around grain boundaries in TNM-0.4 B and TNM-0.8 B alloy, and when the content of B increased to 1.2%, the curved Ti B phases were reduced, while the tiny and straight Ti B phases increased. With further increasing B content to 1.6% and 2.0%, the tiny and straight Ti B phases were coarser. Compressive testing results showed that the mechanical properties of the TNM alloy were enhanced with increasing B content. The maximum strength and strain of TNM alloy were 2339 MPa and33.7% with 1.6% B addition. The compressive strength and strain were mainly enhanced via refinement of lamellar colony and formation of Ti B, and it is found that pile-up of dislocations and deformed twins promoted by Ti B are predominant in improving the mechanical properties of TNM alloys with higher strength and strain. | Yingmei Tan Ruirun Chen Hongze Fang Yangli Liu Hongzhi Cui Yanqing Su Jingjie Guo Hengzhi Fu | 2022 | Journal of Materials Science & Technology2022，，7： | 2 |
您所在的机构暂未开通此部分的功能，请联系管理员