题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | Sintering of WC-Co powder with nanocrystalline WC by spark plasma sintering显示文摘A 92WC-8Co powder mixture with 33 nm WC grains was prepared by strengthening ball milling and was then sintered by spark plasma sintering (SPS) at 1000-1200°C for 5-18 min under 10-25 kN, respectively. Movement of the posi-tion of low punch shown shrinkage of the sintered body began above 800°C. The shrinkage slowly rose as the temperature rose from 800 to 1000°C and then quickly rose at above 1000°C and then gradually rose at above 1150°C. The densities of the samples increased with an increase in sintering temperature, rapidly below 1100°C, and then gradually above 1100°C. WC grains grow gradually with increasing sintering temperature. The powder was sintered to near full density at 1100°C for 5 min under 10 kN. The best result of the sample with 275 nm WC grains and no pores was obtained at 1150°C under 10 kN for 5 min. The research found the graphite die had a function of carburization, which could compensate the sintered body for the lack of carbon, and had the normal microstructure. | WANG Xingqing XIE Yingfang GUO Hailiang O.Van der Biest J.Vleugels | 2006 | Rare Metals2006，25，3： | 7 |
| 2 | Y_2O_3液相掺杂ZrO_2粉体的制备及其特性显示文摘用一种新的液相掺杂技术制备Y2 O3 掺杂的ZrO2 纳米粉体 .在水 -乙醇溶剂中 ,干燥由硝酸铝、硝酸钇和单斜相氧化锆粉体组成的悬浮液 ,然后在 6 0 0℃热分解 ,可以制备出粒度小于 10 0nm的Y2 O3 掺杂单斜相ZrO2 粉体 .这种粉体可以在 0 .1Pa的真空中 ,经 14 5 0℃热压烧结成致密化Y -TZP材料 .此材料的断裂韧性 (KⅠc)为 9.9MPa·m1 /2 ,Vickers硬度 (HV1 0 0N)为 11.72 | 袁正希 Vleugels J Van Der Biest O | 2001 | 硅酸盐学报2001，29，5： | 6 |
| 3 | 含氧化锆的氧化物系统计算相图研究与进展显示文摘氧化锆是一种重要的高性能陶瓷材料,由于其优良的力学和电学性能,在结构陶瓷和功能陶瓷两个方面都有着广泛的应用前景.本文在简述计算相图发展和原理的基础上,综述了近年来对含氧化锆系统计算相图的研究,总结了一些重要体系的研究结果,指出计算相图方法将对该系统材料的组分设计起重大的促进作用. | 许涛 王佩玲 李麟 Omer Van Der Biest Jef Vlengels | 2002 | 无机材料学报2002，17，3： | 3 |
| 4 | 以MH_2(M=Ti,Zr)为原料反应烧结制备MB_2-SiC复相陶瓷显示文摘分别以TiH2,ZrH2为原料,结合原位反应与脉冲电流辅助烧结制备了TiB2-SiC及ZrB2-SiC复相陶瓷。研究发现,所制备的复相陶瓷表现出一定的织构化现象,TiB2及ZrB2晶粒在反应烧结过程中其(001)面沿垂直压力和电流方向生长。金属氢化物粉体的粒径大小对复相陶瓷的致密化及微结构有较大影响:粒径越小越有利于陶瓷的致密化和硼化物晶粒的定向生长。由于金属硼化物的定向,复相陶瓷的机械性能表现出各向异性。TiB2-SiC复相陶瓷具有较高的断裂韧性,最高可达7.3 MPa.m1/2,而ZrB2-SiC复相陶瓷具有更高的抗弯强度(937 MPa)。 | 冉松林 汪德文 Huang Shui-gen Van der Biest Omer Vleugels Jef | 2013 | 人工晶体学报2013，42，4： | 2 |
| 5 | Computer simulation of W-C-Co-V system diffusion couples显示文摘Diffusion couples,WC/Co-1at.%C,V8C7/Co,and WC/Co-0.3wt.%V8C7 were constructed and annealed at tem-peratures ranging from 1100 to 1300°C. The concentration profile of V and W atoms in these couples were measured by EPMA. Aided by Thermo-calc & DICTRA software package,the concentration profiles of W and V in established diffu-sion couples were calculated by the moving boundary model according to revised dynamic parameters and MOB database,respectively. Then the concentration profile of W in Co binder during sintering WC-Co cemented carbide was simulated by the Cell model. It can provide reference for composition and sintering process design of cemented carbides with high per-formance. Meanwhile,the validity of revised dynamic parameters of the W-C-Co-V system is verified by the comparison of experimental and simulated results. | HE Yanlin LI Lin HUANG Shuigen Jef Vleugels Omer Van der Biest | 2007 | Rare Metals2007，26，5： | 2 |
| 6 | Development, characterization and oxidation behavior of Si3N4-Al2O3 ceramics显示文摘 | Vleugels J Van Der Biest O | 1994 | J Europ Ceram Soc1994，28，10： | 1 |
| 7 | Development of ZrO2-ZrB2 composites 显示文摘 | Basu B Vleugels J Van Der Biest O | 2002 | Alloys and Composites2002，334，： | 1 |
| 8 | ZrB2-SiC Composites Prepared by Reactive Pulsed Electric Current Sintering显示文摘 | Ran S Van der Biest O Vleugels J | 2010 | Journal of the European Ceramic Society2010，30，12： | 1 |
| 9 | Electrophoretic depositionof zirconia layers for thermal barrier coatings显示文摘 | van der Biest O Joos E Vleugels J | 2006 | J Mater Sci2006，41，： | 1 |
| 10 | The effect of electrolyte conductivity on electrophoretic deposition显示文摘 | Stappers L Zhang L Van der Biest O | 2008 | Journal of Colloid and Interface Science2008，328，2： | 1 |
| 11 | The role of chemical wear in machining iron based materials by PCD and PCBN super-hard tool materials显示文摘 | Gimenez S Van der Biest O Vleugels J | 2007 | Diamond and Related Materials2007，16，3： | 1 |
| 12 | Calculation of the Quasiternary Systems:Si_3N_4-Y_2O_3-SiO_2,Y_2O_3-SiO_2-BeO and Y_2O_3-Al_2O_3-BeO显示文摘Based on the thermodynamic model of Kaufman for the calculation of quasibinary and quasiternary system, numerical method for the calculation of stable equilibrium is developed and thermodynamic data of undefined phases are discussed in this work for several ceramic systems.The calculated isothermal sections in Si3N4-Y2O3-SiO2 system meet well with other previous calculated phase diagrams and experimental results. The diagrams in Y2O3-SiO2-BeO and Y2O3-Al2O3-BeO systems are calculated for the approach of prediction. | Lin LI(Dept. Materials Science and Engineering, Shanghai University, Shanghai, 200072, China)Qing AO (Dept. of Materials Engineering, Shandong Polytechnic University, Jinan, 250014, China)O. Van Der Biest P Wollants and L.Delaey (Dept. MTM, Katholieke Un | 1995 | Journal of Materials Science & Technology1995，11，4： | 1 |
| 13 | In Situ Platelet-toughened TiB2-SIC Composites Prepared by Reactive Pulsed Electric Current Sintering显示文摘 | Ran S Van der Biest O Vleugels J | 2011 | Scripca Materialia2011，64，12： | 1 |
| 14 | Wire based additive layer manufacturing: Comparison of microstructure and mechanical properties of Ti–6Al–4V components fabricated by laser-beam deposition and shaped metal deposition显示文摘 | Bernd Baufeld Erhard Brandl Omer van der Biest | 2011 | Journal of Materials Processing Tech2011，，6： | 1 |
| 15 | Modeling of Nucleation and Growth of M_(23)C_6 Carbide in Multi-component Fe-based Alloy显示文摘Three-dimensional atom probe (3DAP) technique has been used to study the nucleation and growth of M23C6 carbide in a supersaturated multi-component Fe-based alloy aged at 800°C. 3D images indicate that the radius of M23C6 carbide after ageing for 10 min is about 9 nm. Concentration profiles of alloy elements in the carbide are also obtained. Combined with PANDAT and Thermo-Calc software, attempts to model the early stages of precipitation are present. The calculated particle size and composition of M23C6 carbide is in good agreement with 3DAP data. | Naqiong Zhu Yanlin He Wenqing Liu Lin Li Shuigen Huang Jef Vleugels Omer Van der Biest | 2011 | Journal of Materials Science & Technology2011，27，8： | 1 |
| 16 | Thermal expansion and lattice parameters of shaped metal deposited Ti–6Al–4V显示文摘 | Akhilesh Kumar Swarnakar Omer Van der Biest Bernd Baufeld | 2010 | Journal of Alloys and Compounds2010，，6： | 1 |
| 17 | Removal of low molecular weight components during thermal debinding of powder compacts显示文摘 | Angermann H H Yang F K Van Der Biest O | 1992 | Journal of Materials Science1992，27，9： | 1 |
| 18 | Influence of the oxygen partial pressure on the reduction of CeO2 and CeO2 -ZrO2 ceram- ic-s 显示文摘 | Huang S Li L Biest O Van der | 2005 | Solid State Sciences2005，7，： | 1 |
| 19 | Additive manufacturing of Ti–6Al–4V components by shaped metal deposition: Microstructure and mechanical properties显示文摘 | Bernd Baufeld Omer Van der Biest Rosemary Gault | 2009 | Materials and Design2009，，： | 1 |
| 20 | Synthesis and characterization of Cr 2 AlC ceramics prepared by spark plasma sintering显示文摘 | Wubian Tian Kim Vanmeensel Peiling Wang Guojun Zhang Yongxiang Li Jozef Vleugels Omer Van der Biest | 2007 | Materials Letters2007，，： | 1 |