|
|
|
题名
|
作者
|
年代
|
出处
|
被引量
|
| 1 | High-performance magnesium ion asymmetric Ppy@FeOOH//Mn3O4 micro-supercapacitor显示文摘Micro-supercapacitors(MSCs)are attractive electrochemical energy storage devices owing to their high power density and extended cycling stability.However,relatively low areal energy density still hinders their practical applications.Here,an asymmetric Mg ion MSC with promising high energy density is fabricated.Firstly,indium tin oxide(ITO)NWs were synthesized by chemical vapor deposition as the excellent current collector.Subsequently,nanostructured Mn_(3)O_(4)and Ppy@FeOOH were deposited on the laser-engraved interdigital structure ITO NWs electrodes as the positive and negative electrodes,respectively.Beneficial from the hierarchical micro-nano structures of active materials,high conductive electron transport pathways,and charge-balanced asymmetric electrodes,the obtained MSC possesses a high potential window of 2.2 V and a high areal capacitance of 107.3 mF cm^(-2)at 0.2 mA cm^(-2).The insitu XRD,VSM,and ex-situ XPS results reveal that the primary energy storage mechanism of Mg ions in negative FeOOH electrode is Mg ions de-/intercalation and phase transition reaction of FeOOH.Furthermore,the MSC exhibits a high specific energy density of 71.18μWh cm^(-2)at a power density of 0.22 mWh cm^(-2)and capacitance retention of 85%after 5000 cycles with unvaried Coulombic efficiency.These results suggest promising applications of our MSC in miniaturized energy storage devices. | Xueliang Lv Yaxiong Zhang Xijuan Li Zhiye Fan Guo Liu Wenjian Zhang Jinyuan Zhou Erqing Xie Zhenxing Zhang | 2022 | Journal of Energy Chemistry2022，31，9： | 1 |
| 2 | High energy and insensitive explosives based on energetic porous aromatic frameworks显示文摘The design and synthesis of energetic materials with a compatibility of high energy and insensitivity have always been the research fronts in military and civilian fields.Considering excellent performances of porous organic frameworks and the lack of research in the field of energetic materials,in this study,a new concept named energetic porous aromatic frameworks(EPAFs)is proposed.The strategy of coating high energy explosives such as 2,4,6,8,10,12-hexanitro-2,4,6,8,10,12-hexaazaisowurtzitane(CL-20)and 1,3,5,7-tetranitro-1,3,5,7-tetrazocane(HMX)in the EPAFs by wet-infiltration method has successfully realized the assembly of target energetic composite materials.The results show that the 75 wt.%CL-20@EPAF-1 possesses the safer impact sensitivity of 31.4 J than that of CL-20(4.0 J).Notably,for 75 wt.%CL-20@EPAF-1,in addition to the superior detonation performances of the detonation velocity(8,761 m·s^(-1))and detonation pressure(31.27 GPa),the synergistic effect of the nitrogen-rich EPAFs and the nitramines high energy explosives results in a higher heat of detonation that surpasses the most of pristine high explosives and reported novel energetic materials.In prospect,energetic porous aromatic frameworks could be a promising and inspiring strategy to build high energy insensitive energetic materials. | Jian Song Yansong Shi YaoLu Qinghai Shu Yuyang Tian Fengchao Cui Xiaosong Duli Xijuan Lv Shaohua Jin Guangshan Zhu | 2022 | Nano Research2022，15，2： | 1 |
| 3 | Two‑Dimensional Cr_(5)Te_(8)@Graphite Heterostructure for Efficient Electromagnetic Microwave Absorption显示文摘Two-dimensional(2D)transition metal chalcogenides(TMCs)hold great promise as novel microwave absorption materials owing to their interlayer interactions and unique magnetoelectric properties.However,overcoming the impedance mismatch at the low loading is still a challenge for TMCs due to the restricted loss pathways caused by their high-density characteristic.Here,an interface engineering based on the heterostructure of 2D Cr_(5)Te_(8) and graphite is in situ constructed via a one-step chemical vapor deposit to modulate impedance matching and introduce multiple attenuation mechanisms.Intriguingly,the Cr_(5)Te_(8)@EG(ECT)heterostructure exhibits a minimum reflection loss of up to−57.6 dB at 15.4 GHz with a thin thickness of only 1.4 mm under a low filling rate of 10%.The density functional theory calculations confirm that the splendid performance of ECT heterostructure primarily derives from charge redistribution at the abundant intimate interfaces,thereby reinforcing interfacial polarization loss.Furthermore,the ECT coating displays a remarkable radar cross section reduction of 31.9 dB m^(2),demonstrating a great radar microwave scattering ability.This work sheds light on the interfacial coupled stimulus response mechanism of TMC-based heterogeneous structures and provides a feasible strategy to manipulate high-quality TMCs for excellent microwave absorbers. | Liyuan Qin Ziyang Guo Shuai Zhao Denan Kong Wei Jiang Ruibin Liu Xijuan Lv Jiadong Zhou Qinghai Shu | 2024 | Nano-Micro Letters2024，16，3： | 0 |
| 4 | Anti-aging performance improvement and enhanced combustion efficiency of boron via the coating of PDA显示文摘Boron is an ambitious fuel in energetic materials since its high heat release values,but its application is prohibited by low combustion efficiency and oxidization during storage.The polydopamine(PDA)was introduced into boron particles,investigating the impact of PDA content on the energetic behavior of boron.The results indicated that the PDA coating formed a fishing net structure on the surface of boron particles.The heat release results showed that the combustion calorific value of B@PDA was higher than that of the raw boron.Specifically,the actual combustion heat of boron powder in B@10%PDA increased by 38.08%.Meanwhile,the DSC peak temperature decreased by 100.65℃under similar oxidation rate compared to raw boron.Simultaneously,the B@PDA@AP and B@AP composites were prepared,and their combustion properties were evaluated.It was demonstrated that B@10%PDA@AP exhibited superior performance in terms of peak pressure and burning time,respectively.The peak pressure is 12.43 kPa more than B@AP and burning time is 2.22 times higher than B@AP.Therefore,the coating of PDA effectively inhibits the oxidization of boron during storage and enhances the energetic behavior of boron and corresponding composites. | Shuai Ma Qinghai Shu Mengyang Zhang Hongyu Huang Yansong Shi Xijuan Lv Shuai Zhao | 2024 | Defence Technology(防务技术)2024，33，3： | 0 |
您所在的机构暂未开通此部分的功能，请联系管理员